AISI 301 1.4310 Stainless Steel Strip 2B BA soft annealed 1/2H 3/4H H hardness
Specification:
| Product Name | 301 Stainless steel coil/strip |
| Process | Hot Rolled/Cold Rolled |
| Grade | 200/300/400 series(301 310s 309s 304 316 316l 201 202 321 410 430......) |
| Surface | No.1/ 2B/ BA/No.4/ HL |
| Standard | AISI ASTM JIS EN DIN ...... |
| Thickness | 0.2-3mm(cold rolled) 3-6mm(hot rolled) |
| Width | 5mm ~ 600mm |
Chemical Composition:
| Element | Percent by Weight Maximum Unless Range is Specified |
| Carbon | 0.15 maximum |
| Manganese | 2.00 maximum |
| Phosphorus | 0.045 maximum |
| Sulfur | 0.030 maximum |
| Silicon | 0.75 maximum |
| Chromium | 16.00-18.00 |
| Nickel | 6.00-8.00 |
| Nitrogen | 0.10 maximum |
Mechanical properties:
| Condition | Tensile Strength, Min. Ksi(MPa) | 0.2% Yield Strength, Min. Ksi (MPa) | Elong. In 2" (50mm) %, Min. | ||
| Annealed | 75 | 515 | 30 | 205 | 40 |
| 1/4 Hard | 125 | 862 | 75 | 517 | 25 |
| 1/2 Hard | 150 | 1,034 | 110 | 758 | 18 |
| 3/4 Hard | 175 | 1,207 | 125 | 931 | 12 |
| Full Hard | 185 | 1,276 | 140 | 965 | 9 |
Tempered:
|
Temper |
Condition | Tension | ||||||||||
| Longitudinal | Transverse | |||||||||||
|
0.2% Y.S. Ksi (MPa) |
Modulus 10 6psi (GPa) |
0.2% Y.S. Ksi (MPa) |
Modulus 10 6psi (GPa) | |||||||||
| Annealed 1/4 Hard | As annealed As rolled Stress relieved | 36 80 77 | (248) (552) (531) | 31.0 28.0 28.7 | (214) (193) (198) | 36 84 79 | (248) (579) (545) | 30.6 28.6 27.0 | (211) (197) (186) | |||
| 1/2 Hard | As rolled Stress relieved | 122 128 | (841) (883) | 26.8 27.9 | (185) (192) | 123 130 | (848) (896) | 28.1 28.6 | (194) (197) | |||
| 3/4 Hard | As rolled Stress relieved | 142 155 | (979) (1,069) | 25.8 27.3 | (178) (188) | 145 155 | (1,000) (1,069) | 27.5 28.8 | (190) (199) | |||
| Full Hard | As rolled Stress relieved | 160 175 | (1,103) (1,207) | 25.2 28.4 | (174) (196) | 163 181 | (1,124) (1,248) | 28.4 30.5 | (196) (210) | |||
| Compression | ||||||||||||
| Annealed 1/4 Hard | As annealed As rolled Stress relieved | 38 50 73 | (262) (345) (503) | 30.6 28.2 28.8 | (211) (194) (199) | 38 91 84 | (262) (627) (579) | 30.3 28.2 30.6 | (209) (194) (211) | |||
| 1/2 Hard | As rolled Stress relieved | 90 111 | (621) (765) | 27.5 29.2 | (190) (201) | 142 144 | (979) (993) | 27.5 29.8 | (190) (205) | |||
| 3/4 Hard | As rolled Stress relieved | 100 133 | (690) (917) | 26.5 27.5 | (183) (190) | 170 176 | (1,172) (1,213) | 27.9 29.5 | (192) (203) | |||
| Full Hard | As rolled Stress relieved | 115 169 | (793) (1,165) | 24.6 27.7 | (170) (191) | 191 209 | (1,317) (1,441) | 29.4 29.6 | (203) (204) | |||